materials:borosilicate glass
used in lever gauge in boiler for water position.
Thickness: 10mm-25mm
Diameter: 50mm - 250m
Port: Xingang seaport
Minimum Order Quantity: 100 Piece/Pieces
Supply Ability: 12000 Piece/Pieces per Year
Payment Terms: L/C,T/T,Western Union
Contact SupplierPackaging Detail: each packed in white paper box,then 50-60piece packed in carton.
Delivery Detail: within 20 day,after received your 30% T/T in advance
Level Gauge Glass
It is also named Reflex Gauge Glass,Sight Glass,Reflex Glasses,Reflex Sight Glass,Spares for level gauge,Boiled Gauge Glass,Boiled Parts,ect
Description
Level Gauge Glass is made from Borosilicate with toughened process.
It is used in lever gauge in boiler for water position.
Style:
1)Reflex glass
2)Transparent glass
3)Round sight glass
4)Gsket for glass
Dimensions
1) Reflex glass, available size:
400 x 34(30) x 17mm, 370 x 34(30) x 17mm, 340 x 34(30) x 17mm
320 x 34(30) x 17mm, 300 x 34(30) x 17mm, 280 x 34(30) x 17mm
250 x 34(30) x 17mm, 218 x 34(30) x 17mm, 190 x 34(30) x 17mm
165 x 34(30) x 17mm, 140 x 34(30) x 17mm, 115 x 34(30) x 17mm
The other size is optional or according to the requirements of customers.
Working temperature: 260 degree C, Working pressure: 4.0MPa
2) Transparent plane (without grooves)
The available size same as reflex glass.
Working temperature: 260 degree C, Working pressure: 8.0 MPa
3) Round glass
Thickness: 10mm-25mm
Diameter: 50mm - 250mm
Pressure: 6 - 25 bar
Temperature: 250 degree C
4) Gasket for glass
Asbestos gasket and non-asbestos gasket
Level Gauge Glass Physical Property | |
Testing Item | Standard Rules |
1. Appearance | 1) Air bubble: Diameter≤0.5mm,in the 10mm x 10mm area the quantity must be ≤3. Diameter from 0.5mm to 1.5mm dispersive air bubble,there is less 2 on the sight plane and less 5 on the No-sight plane. Their distance must be >40mm. The air bubble of Diameter from 1.5mm to 2mm ≤3 on the No-sight plane. Their distance must >40mm. On the sight plane, The distance to the side in 7.5mm,the air bubble of the diameter<1mm mustn’t be more 2. 2) The glass don’t allow slag and scrap iron,etc. impurity. 3) Stripe : don’t allow have palpable filaceous and pectinate stripe on the sight plane. 4) Cockle: In the side face,don’t allow have the cockle of depth .>1mm. 5) Crack: don’t allow have crack. 6) Scrape: On the sight plane and in the 7.5mm to edge,the scrape of less than 10mm don’t allow more 2 strips. 7) The sight plane must be polishing,and sealing side must be rubbing and polishing. |
2. Colour and Lustre | It should be no color and transparent,and with its self tine green is allowed. |
3. Water-resistance | Cooked in the water for 5 hours,then weigh up ,then titration with 25ml 0~31 ug/g |
4. Alkali-resistance | Cooked in the 0.5N NaoH for 3 hours,then Weigh up,weightlessness should be ≤75 mg/dm2 |
5. Temperature-resistance impacts capability | Put it into electric cooker,keep for 7min under the temperature of 260°C±1°C,then,put into the water of 20±1°C,it should not crack |
6. Bend-resistance | ≥80 MPa |