boiler gauge glass
Its made from Borosilicate, it is used in lever gauge in boiler for water position.
It is also named: Reflex Gauge Glass, Sight glass, Reflex Glasses
Reflex sight glass, Spares For level Gauge
Plane transparent
Transparent plane
340 x 34 x 17mm, 320 x 34 x 17mm, 280 x 34 x 17mm
250 x 34 x 17mm, 218 x 34 x 17mm, 216 x 34 x 17mm
190 x 34 x 17mm, 165 x 34 x 17mm, 215 x 34 x 22mm
218 x 38 x 23mm, 190 x 38 x 23mm, 165 x 38 x 23mm
The other size is optional or according to the requirements of customers.
Working temperature: 260 , Working pressure: 8.0 MPa
The materialBorosilicate Glass
Level Gauge Glass Physical Property
Testing Item | Standard Rules |
1. Appearance | 1) Air bubble: Diameter≤0.5mm,in the 10mm x 10mm area the quantity must be ≤3. Diameter from 0.5mm to 1.5mm dispersive air bubble,there is less 2 on the sight plane and less 5 on the No-sight plane. Their distance must be 40mm. The air bubble of Diameter from 1.5mm to 2mm ≤3 on the No-sight plane. Their distance must 40mm. On the sight plane, The distance to the side in 7.5mm,the air bubble of the diameter1mm mustnt be more 2. 2) The glass dont allow slag and scrap iron,etc. impurity. 3) Stripe : dont allow have palpable filaceous and pectinate stripe on the sight plane. 4) Cockle: In the side face,dont allow have the cockle of depth 1mm. 5) Crack: dont allow have crack. 6) Scrape: On the sight plane and in the 7.5mm to edge,the scrape of less than 10mm dont allow more 2 strips. 7) The sight plane must be polishing,and sealing side must be rubbing and polishing. |
2. Colour and Lustre | It should be no color and transparent,and with its self tine green is allowed. |
3. Water-resistance | Cooked in the water for 5 hours,then weigh up ,then titration with 25ml 0~31 ug/g |
4. Alkali-resistance | Cooked in the 0.5N NaoH for 3 hours,then Weigh up,weightlessness should be ≤75 mg/dm2 |
5. Temperature-resistance impacts capability | Put it into electric cooker,keep for 7min under the temperature of 260±1,then,put into the water of 20±1,it should not crack. |
6. Bend-resistance | ≥80 MPa |