Passive Q-switch Cr4+:YAG
Cr4+:YAG is an excellent passive Q-switch or saturable absorber crystal of choice for 1μm Nd lasers.
Advantages of Cr4+:YAG Crystals
Specifications
Orientation | [100] or [111] within 5° |
Initial absoption coefficience: | 0.5~6cm-1@1064nm |
Initial transmission | 5%~95%@1064nm |
Dimension | Diameter:3~12mm HxW:3x3~12x12mm |
Dimensional tolerances | Diameter+0.000"/-0.002",H&W±0.002" |
Barrel finish | Ground Finish400# Grit |
Parallelism | ≤30" |
Flatness | λ/8 |
Surface quality | 20-10(MIL-O-13830A) |
Damage threshold | ≥500MW/cm2 |
AR coating reflectivity | ≤0.25% (@1064nm) |
Physical and Chemical Properties
Crystal Structure | Cubic |
Lattice Parameters | 12.01 Å |
Melting Point | 1970°C |
Moh Hardness | 8.5 |
Density | 4.56±0.04g/cm3 |
Specific Heat (0-20) | 0.59J/g.cm3 |
Modulus of Elasticity | 310GPa |
Young's Modulus | 3.17×104Kg/mm2 |
(est.)Poisson Ratio | 0.3(est.) |
Tensile Strength | 0.13~0.26GPa |
Thermal Expansion Coefficient | [100]Direction:8.2×10-6/°C(0~250°C) [110]Direction:7.7×10-6/°C(0~250°C) [111]Direction:7.8×10-6/°C(0~250°C) |
Thermal Conductivity | 14W/m/K(@20°C) 10.5W/m/K(@100°C) |
Thermal Optical Coefficient (dn/dT) | |
Thermal Shock Resistance | 790W/m |
Solubility | Water: Insoluble; Common Acids: Slightly |